'Structural steel' is
steel construction
material, a
profile, formed with a specific
shape or
cross section and certain standards of
chemical composition and strength. Structural steel shape, size, composition, strength, storage, etc, is regulated in most industrialised countries.
A steel
I-beam, in this case used to support wooden beams in a house. The I-beam is probably the most recognizable structural steel element: I-beams and related shapes are used widely in all-steel construction and composite construction with
concrete, wood, or other structural materials.
Steel is sometimes described as a sea of
electrons.
Protons are virtually surrounded by electrons. It is easy to see how the addition of
heat first causes expansion and then softening, to the point of liquification. That is how steel is manufactured and that is how it acts as a structural element in a building fire. Proper
fireproofing mitigates this. Still, care must be taken to ensure that expansion of structural elements does not damage wall and floor assemblies required to have a
fire-resistance rating. Of particular concern are any
penetrants in a
firewalls and ferrous
cable trays in organic
firestops.
Steel beam through-penetration. The
firestop surrounding the beam is incomplete - packing only, sealant is yet to be applied. The beam itself must be treated with
fireproofing to prevent it from twisting and damaging the wall during a fire. The
beam is the
penetrant.
Common structural shapes
In most
developed countries, the shapes available are set out in published standards, although a number of specialist and proprietary
cross sections are also available.
★
I-beam (I-shaped cross-section - in Britain these include Universal Beams (UB) and Universal Columns (UC); in Europe it includes the IPE, HE, HL, HD and other sections; in the US it includes Wide Flange (WF) and H sections)
★ Z-Shape (half a flange in opposite directions)
★ HSS-Shape (
Hollow structural section also known as SHS (structural hollow section) and including
square,
rectangular,
circular (
pipe) and
elliptical cross-sections)
★ Angle (L-shaped cross-section)
★ Channel (C-shaped cross-section)
★ Tee (T-shaped cross-section)
★
Rail profile (asymmetrical I-beam)
★
★
Railway rail
★
★
Vignoles rail
★
★
Flanged T rail
★
★
Grooved rail
★ Bar, a piece of
metal,
rectangular cross sectioned (flat) and long, but not so wide so as to be called a
sheet.
★ Rod, a
round or
square and long piece of
metal or
wood, see also
rebar.
★ Plate,
sheet metal thicker than 6 mm or 1/4 in.
While many sections are made by hot or cold
rolling, others are made by
welding together flat or bent plates (for example, the largest circular hollow sections are made from flat plate bent into a circle and seam-welded).
Structural steels
Most industrialised countries prescribe a range of standard steel grades with different strengths, corrosion resistance and other properties.
Standard structural steels (Europe)
Most steels used throughout Europe are specified to comply with the
European standard EN 10025. However, many national standards also remain in force.
Typical grades are described as 'S275J2' or 'S355K2W'. In these examples, 'S' denotes structural rather than engineering steel; 275 or 355 denotes the
yield strength in newtons per square millimetre or the equivalent
megapascals; J2 or K2 denotes the materials
toughness by reference to
Charpy impact test values; and the 'W' denotes
weathering steel. Further letters can be used to designate
normalised steel ('N' or 'NL');
quenched and tempered steel ('Q' or 'QL'); and thermomechanically rolled steel ('M' or 'ML').
The normal yield strength grades available are 195, 235, 275, 355, 420, and 460, although some grades are more commonly used than others e.g. in the UK, almost all structural steel is grades S275 and S355. Higher grades are available in quenched and tempered material (500, 550, 620, 690, 890 and 960 - although grades above 690 receive little if any use in construction at present).
Standard structural steels (USA)
Steels used for building construction in the US use standard alloys identified and specified by
ASTM International. These steels have an alloy identification beginning with 'A' and then two, three, or four numbers. The four-number
AISI steel grades commonly used for mechanical engineering, machines, and vehicles are a completely different specification series.
The standard commonly used structural steels are:
[1]
Carbon steels
★
A36 - structural shapes and plate
★
A53 - structural pipe and tubing
★
A500 - structural pipe and tubing
★
A501 - structural pipe and tubing
★
A529 - structural shapes and plates
High strength low alloy steels
★
A441 - structural shapes and plates
★
A572 - structural shapes and plates
★
A618 - structural pipe and tubing
★
A992 - W shapes beams only
Corrosion resistant high strength low alloy steels
★
A242 - structural shapes and plates
★
A588 aka Cor-ten - structural shapes and plates
Quenched and tempered alloy steels
★
A514 - structural shapes and plates
★
A517 - boilers and pressure vessels
Steel vs. concrete
As raw material prices fluctuate, often so does building design. During times of lower steel prices, more steel and less
concrete is used, and vice versa. Each set of vendors and users typically maintain national industry associations that advocate the use of its materials versus the other. However, both materials are really needed together. Concrete without steel re-enforcement (usually ribbed round bars called
Rebar) is not structurally sound. Steel on its own, without solid concrete floors, is likewise not a preferred building method.
While rebar is almost always steel, it is not considered a structural steel and is described separately in the
Rebar and
Reinforced concrete articles.
Critical, and melting temperatures of structural steel
Most people do not realize that most of the properties of steel vary widely, based on what alloying elements are in it, and, for steel with carbon as it's only alloying element, how much carbon is present.
The critical temperature for steel starts at 900°C for pure iron, then, as more carbon is added, the temperature falls to a minimum 724°C for
eutectic steel (steel with only .83% by weight of carbon in it). As 2.1 % carbon (by weight) is approached, the critical temperature climbs back up, to 1130°C.
This is not to be confused with the
critical temperature for a fluid. The term "critical temperature", when used in regard to steel, means the temperature that all of the carbon in a steel is transformed into an ''austenitic crystal structure''. This is very important for heat-treating steels.
Melting Point of Carbon only Steels
The bare minimum temperature that any alloy of Steel begins to melt is 1130°C. Steel never turns into a liquid below this temperature. Pure Iron ('Steel' with 0% Carbon) starts to melt at 1492°C (2720°F), and is completely liquid upon reaching 1539°C (2802°F). Steel with 2.1% Carbon by weight begins melting at 1130°C (2066°F), and is completely molten upon reaching 1315°C (2400°F) 'Steel' with more than 2.1% Carbon is no longer Steel, but is known as
Cast iron.
http://www.msm.cam.ac.uk/phase-trans/images/FeC.gif
Fire protection with steel vs. competition
Structural steel requires external insulation in order to prevent the steel from absorbing enough energy to reach this temperature. First, steel expands, when heated, and once enough energy has been absorbed, it softens and loses its structural integrity. This is easily prevented through the use of
fireproofing. Likewise, although concrete structures on their own are able to achieve fire-resistance ratings, concrete is also subject to severe spalling, especially with elevated moisture inside the concrete at the time it becomes exposed to fire. There is also fireproofing available for concrete but this is typically not used in buildings. Instead, it is used in traffic tunnels and locations where a
hydrocarbon fire is likely to break out. Thus, steel and concrete compete against one another not only on the basis of the price per unit of mass but also on the basis of the pricing for the fireproofing that must be added in order to satisfy the
passive fire protection requirements that are mandated through
building codes. Common fireproofing methods for structural steel include
intumescent,
endothermic and
plaster coatings.
See also
References
1. 'Manual of Steel Construction, 8th Edition', 2nd revised printing, American Institute of Steel Construction, 1987, ch 1 page 1-5
External links
★
The American Institute of Steel Construction, Inc.
★
Product Data Standards for Structural Steel (CIS/2, IFC)
العربية
中国
Français
Deutsch
Ελληνική
हिन्दी
Italiano
日本語
Português
Русский
Español